Z.-S. Wu, W. Ren*, L. Xu, F. Li, H.-M. Cheng*, 
Acs Nano 2011, 5 (7): 5463-5471.  
DOI:10.1021/nn2006249  [PDF]

发布时间:2016-03-18    栏目名称:2011

Z.-S. Wu, W. Ren*, L. Xu, F. Li, H.-M. Cheng*,
Acs Nano 2011, 5 (7): 5463-5471. 
DOI:10.1021/nn2006249  [PDF]

Abstract:
One great challenge in the development of lithium ion batteries is to simultaneously achieve high power and large energy capacity at fast charge and discharge rates for several minutes to seconds. Here we show that nitrogen- or boron-doped graphene can be used as a promising anode for high-power and high-energy lithium ion batteries under high-rate charge and discharge conditions. The doped graphene shows a high reversible capacity of >1040 mAh g–1at a low rate of 50 mA g–1. More importantly, it can be quickly charged and discharged in a very short time of 1 h to several tens of seconds together with high-rate capability and excellent long-term cyclability. For example, a very high capacity of ~199 and 235 mAh g–1 was obtained for the N-doped graphene and B-doped graphene at 25 A g–1 (about 30 s to full charge). We believe that the unique two-dimensional structure, disordered surface morphology, heteroatomic defects, better electrode/electrolyte wettability, increased intersheet distance, improved electrical conductivity, and thermal stability of the doped graphene are beneficial to rapid surface Li+absorption and ultrafast Li+ diffusion and electron transport, and thus make the doped materials superior to those of pristine chemically derived graphene and other carbonaceous materials.

中国科学院大连化学物理研究所

大连市中山路457号

邮编:116023

版权所有 © 二维材料化学与能源应用研究组

首页 / 组长简介 / 研究方向 / 研究组成员 / 发表论文 / 新闻 / 联系我们