Z.-S. Wu, Y. Sun, Y.-Z. Tan, S. Yang, X. Feng*, K. Müllen*, 
Journal of the American Chemical Society 2012, 134 (48): 19532-19535.  
DOI:10.1021/ja308676h  [PDF]

发布时间:2016-03-18    栏目名称:2012

Z.-S. Wu, Y. Sun, Y.-Z. Tan, S. Yang, X. Feng*, K. Müllen*,
Journal of the American Chemical Society 2012, 134 (48): 19532-19535. 
DOI:10.1021/ja308676h  [PDF]

Abstract:
Three-dimensional graphene-based frameworks (3D-GFs) with hierarchical macro- and meso-porous structures are presented. The interconnected macropores are derived from hydrothermally assembled 3D graphene aerogels (GAs), while the mesopores are generated by the silica networks uniformly grown on the surface of graphene. The resulting 3D-GFs exhibit narrow mesopore size distribution (2–3.5 nm), high surface area, and low mass density. These intriguing features render 3D-GFs a promising template for creating various 3D porous materials. Specifically, 3D GA-based mesoporous carbons (GA-MC) and metal oxide hybrids (GA-Co3O4, GA-RuO2) can be successfully constructed via a nanocasting technology. Benefiting from the integration of meso- and macroporous structures, 3D GA-MC manifests outstanding specific capacitance (226 F g–1), high rate capability, and excellent cycling stability (no capacitance loss after 5000 cycles) when it is applied in electrochemical capacitors.

中国科学院大连化学物理研究所

大连市中山路457号

邮编:116023

版权所有 © 二维材料化学与能源应用研究组

首页 / 组长简介 / 研究方向 / 研究组成员 / 发表论文 / 新闻 / 联系我们